Synthesis the New Nanostructure Ti0.7Ir0.3O2 via Low Temperature Hydrothermal Process
(Trường Đại học Nguyễn Tất Thành, 2018-02-01) Huynh, Thien Tai; Nguyen, Van At; Pham, Quoc Hau; Bach, Long Giang
In this paper, the novel nanostructure Ti0.7Ir0.3O2 was prepared for the first time via low temperature hydrothermal process. The synthesis process for the new nanostructure Ti0.7Ir0.3O2 was studied in detail in this work. The impact of hydrothermal temperature as well as the reaction time on the dominant phase formation is extensively investigated in this work. We found that the Ti0.7Ir0.3O2 nanoparticles exist in both rutile and anatase phase. We found that the Ti0.7Ir0.3O2 nanoparticles with an irregular spherical shape with particle size of approximately 20-30nm with high crystallinity. In addition, we also found that the optimal condition to synthesize the Ti0.7Ir0.3O2 NPs is obtained at 210oC and 10 hours. The result not only introduces a promising catalyst support Ti0.7Ir0.3O2 for much needed fuel cells, but it also open a new material type of Ir doped TiO2.