Synthesis the New Nanostructure Ti0.7Ir0.3O2 via Low Temperature Hydrothermal Process
Ngày
2018-02-01
Tác giả
Huynh, Thien Tai
Nguyen, Van At
Pham, Quoc Hau
Bach, Long Giang
Tên Tạp chí
Tạp chí ISSN
Nhan đề tập
Nhà xuất bản
Trường Đại học Nguyễn Tất Thành
Giấy phép
Tóm tắt
In this paper, the novel nanostructure Ti0.7Ir0.3O2 was prepared for the first time via low temperature hydrothermal process. The synthesis process for the new nanostructure Ti0.7Ir0.3O2 was studied in detail in this work. The impact of hydrothermal temperature as well as the reaction time on the dominant phase formation is extensively investigated in this work. We found that the Ti0.7Ir0.3O2 nanoparticles exist in both rutile and anatase phase. We found that the Ti0.7Ir0.3O2 nanoparticles with an irregular spherical shape with particle size of approximately 20-30nm with high crystallinity. In addition, we also found that the optimal condition to synthesize the Ti0.7Ir0.3O2 NPs is obtained at 210oC and 10 hours. The result not only introduces a promising catalyst support Ti0.7Ir0.3O2 for much needed fuel cells, but it also open a new material type of Ir doped TiO2.
Mô tả
7 tr.
Từ khóa
Ti0.7Ir0.3O2 , Hydrothermal , Nanostructure