Investigate the effect of hydrothermal temperature on the structure and characterization of 20 % ZnO-Cu2O nanocomposite
Các tập tin
Ngày
2022
Tác giả
Nguyen, Thi Tuyet Mai
Nguyen, Thi Lan
Nguyen, Kim Nga
Ta, Ngoc Dung
Huynh, Dang Chinh
Tên Tạp chí
Tạp chí ISSN
Nhan đề tập
Nhà xuất bản
Nguyen Tat Thanh University
Giấy phép
Tóm tắt
The ZnO with 20 mol.% was hybridized with Cu2O to fabricate nanocomposites (20 % ZnO-Cu2O (ZC NCs)) were prepared by hydrothermal method at the investigated temperatures of (120, 200 and 250) ℃. The structural properties and characterization of the materials were investigated by physical measurements including: XRD, SEM, EDX and solid sample UV-Vis spectra. The results showed that the fabricated material samples consist of two crystalline phases (ZnO wurtzite and Cu2O octahedra) with calculated lattice parameters that were suitable for each type of crystal of the material. The average crystal sizes of the ZC120, ZC200 and ZC250 samples were (20.08, 20.36 and 22.50) nm respectively, which were grown lager when the hydrothermal temperature increase. The optical bandgap energy (Eg) of the ZC120, ZC200 and ZC250 material samples was determined to be (2.51, 2.52 and 2.56) eV, respectively. These Eg values of the fabricated ZC NCs samples were intermediate between the two types of ZnO (Eg 3.37 eV) and Cu2O (Eg 2.17 eV) materials, and was valid in the excitation region of visible light.
Mô tả
7 p.
Từ khóa
Cuprous oxide , ZnO-Cu2O nanocomposite , ZnO doped Cu2O nanoparticles , Visible light irradiation
Trích dẫn
Nguyen Tat Thanh University. (2023). Journal of Science and Technology - NTTU, Volume 6, Issue 1. ISSN 2615-9015.